Influence of Solar Electromagnetic Radiation on the Optical Properties of Micro-, Submicro- and Nanopowders of ZnO

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The diffuse reflection spectra of micro-, submicro- and nanopowders of ZnO after irradiation with solar electromagnetic radiation were researcherd. High purity ZnO powders purchased from Aladdin Chemistry were used. Average particle sizes of the studied powders were: from 800 to 3000 nm for micropowders, from 100 to 300 nm for submicropowders, 20–50 nm for nanopowders. Irradiation of the powders under study with electromagnetic radiation from the Solar was carried out for 2, 5, 10 and 15 h. The research results showed that the reflectivity of the surface of zinc oxide micropowders in the wavelength range from 200 to 2000 nm is higher than that of submicro- and nanopowders. The contribution to the formation of the integral absorption band responsible for the degradation of the optical properties of ZnO micro- and nanopowders is made by induced defects of the cationic sublattice, and of submicropowders — defects of the anionic sublattice and acceptor-donor pairs. Approximately the same intensity of absorption bands of defects in ZnO submicropowders explains the small change in the integral absorption coefficient of solar radiation for this type of powder. This explains the higher radiation resistance of zinc oxide submicropowders to the action of solar spectrum quanta under the same irradiation conditions.

Толық мәтін

Рұқсат жабық

Авторлар туралы

I. Verkhoturova

Аmur State University

Хат алмасуға жауапты Автор.
Email: rusia@mail.ru
Ресей, Blagoveshchensk

V. Neshchimenko

Аmur State University

Email: v1ta1y@mail.ru
Ресей, Blagoveshchensk

M. Mikhailov

Tomsk State University of Control Systems and Radioelectronics

Email: rusia@mail.ru
Ресей, Tomsk

Әдебиет тізімі

  1. Sokolovskiy A., Plis E., Hoffmann R., Bengtson M., Ferguson D. // Surf. Coat. Technol. 2022. V. 451. Р. 129030. https://www.doi.org/10.1016/j.surfcoat.2022.129030
  2. Kiomarsipour N., Razavi R. S., Ghani K. // Dyes and Pigments. 2013. V. 96. P. 403. https://www.doi.org/10.1016/j.dyepig.2012.08.019
  3. Михайлов М.М., Лапин А.Н., Юрьев С.А. // Поверхность. Рентген., синхротр. и нейтрон. исслед. 2021. № 9. С. 63. https://www.doi.org/10.31857/S1028096021090107
  4. Lv J., Yang J., Li X., Chai Z. // Dyes and Pigments. 2019. V. 164. P. 87. https://www.doi.org/10.1016/j.dyepig.2019.01.014
  5. Юрина В.Ю., Дудин А.Н., Нещименко В.В., Михайлов М.М. // Поверхность. Рентген., синхротр. и нейтрон. исслед. 2023. № 2. С. 33. https://www.doi.org/10.17223/00213411/65/8/3
  6. Дудин А.Н., Юрина В.Ю., Нещименко В.В., Ли Ч. // Научно-технические ведомости СПбГПУ. Физико-математические науки. 2022. Т. 15. № 3.1. С. 101. https://www.doi.org/10.18721/JPM.153.117
  7. Lv J., Fang M. // Mater. Lett. 2018. V. 218. P. 18. https://www.doi.org/10.1016/j.matlet.2018.01.137
  8. Neshchimenko V., Li Ch., Mikhailov M., Lv J. // Nanoscale. 2018. V. 10. Iss. 47. P. 22335. https://www.doi.org/10.1039/C8NR04455D
  9. Нещименко В.В., Ли Ч., Михайлов М.М. //Поверхность. Рентген., синхротр. и нейтрон. исслед. 2019. № 1. С. 88. https://www.doi.org/10.1134/S0207352819010165
  10. Нещименко В.В. Структура, свойства и радиационная стойкость оксидных микро- и нанопорошков и отражающих покрытий, изготовленных на их основе: Дис. д-ра физ.-мат. наук: 01.04.07. Томск: ТУСУР, 2017. 273 с.
  11. Mikhailov M.M., Yuryev S.A., Lapin A.N., Karanskiy V.V. // Symmetry. 2020. V. 12. P. 1021. https://www.doi.org/10.3390/sym12061021
  12. Верхотурова И.В., Нещименко В.В., Юрина В.Ю., Бурова А.И. // Вестник АмГУ. Естественные и экономические науки. 2022. № 97. С. 28. https://www.doi.org/10.22250/20730268_2022_97_28
  13. Kositsyn L.G., Mikhailov M.M., Kuznetsov N.Ya., Dvoretskii M.I. // Instrum. Exp. Tech. 1985. V. 28. № 4. P. 929.
  14. ASTM E490-00a. Standard Solar Constant and Zero Air Mass Solar Spectral Irradiance Tables. West Conshohocken: ASTM International, 2019.
  15. ASTM E903-96. Standard Test Method for Solar Absorptance, Reflectance, and Transmittance of Materials Using Integrating Spheres. West Conshohocken: ASTM International, 2012.
  16. Varley J.H.O. // Nature. 1954. V. 174. P. 886.
  17. Воробьев А.А., Завадовская Е.К., Анненков Ю.М., Лисицын В.М., Воробьев В.С. // Известия Томского ордена трудового красного знамени политехнического Института им. С.М. Кирова. 1969. Т. 199. С. 119.
  18. Крегер Ф. Химия несовершенных кристаллов. М.: Мир, 1969. 654 с.

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. SEM images of micro- (a), submicro- (b) and nanopowders (c) of zinc oxide.

Жүктеу (156KB)
Метадеректер
3. Fig. 2. Diffractograms from micro- (1), submicro- (2) and nanopowders (3) of ZnO. The labelled diffraction maxima correspond to the hexagonal structure of wurtzite.

Жүктеу (78KB)
Метадеректер
4. Fig. 3. Diffuse reflectance spectra of micro- (1), nano- (2) and submicro- (3) ZnO powders.

Жүктеу (71KB)
Метадеректер
5. Fig. 4. Dependence of the values of the change in the solar radiation absorption coefficient as micro- (1), nano- (2) and submicro-powders (3) of zinc oxide after irradiation with solar EMI on the exposure time.

Жүктеу (67KB)
Метадеректер
6. Fig. 5. Induced absorption spectra of micro- (a), nano- (b) and submicro-powders (c) of zinc oxide when exposed to EMI for 2 (1); 5 (2); 10 (3); 15 h (4).

Жүктеу (206KB)
Метадеректер
7. Fig. 6. Decomposition into individual bands of the induced absorption spectra of micro- (a), submicro- (b) and nanopowders (c) of zinc oxide after 15 h of EMI exposure.

Жүктеу (276KB)
Метадеректер

© Russian Academy of Sciences, 2025